Hi Kenny, I showed my hub The Man Ring you posted, offering to get it as his Christmas gift. He turned it down as it's 9mm in width. Might be uncomfortable since it's so wide. Anyway, he indicated an interest in alternative wedding band. See my love of jewelry has rubbed off on him
His few complaints about his current band is that the band will be hot when DH is hot. He also complained that it loses it's luster a few months after polish and dings easily. I sent our bands in for polish every 2-3 years. Mine remains shiny for a long while though.
I told him to look thru the titanium band designs and pick one. Then I saw your Octavia thread where you used cobalt chrome. I know you haven't worn the cobalt chrome ring for long though.
I would like advice on which metal he should pick if he wants:
Band to remain cool
Band to not ding easily
More scratch resistant
Needn't be polished as I doubt any jeweler polishes non-precious metal where I stay but I might be wrong
Or any other metal fulfilling the above criteria.
Looking forward to hearing your opinions. Thank you.
His few complaints about his current band is that the band will be hot when DH is hot. He also complained that it loses it's luster a few months after polish and dings easily. I sent our bands in for polish every 2-3 years. Mine remains shiny for a long while though.
I told him to look thru the titanium band designs and pick one. Then I saw your Octavia thread where you used cobalt chrome. I know you haven't worn the cobalt chrome ring for long though.
I would like advice on which metal he should pick if he wants:
Band to remain cool
Band to not ding easily
More scratch resistant
Needn't be polished as I doubt any jeweler polishes non-precious metal where I stay but I might be wrong
Or any other metal fulfilling the above criteria.
Looking forward to hearing your opinions. Thank you.